Electrical interconnection structure formation

ABSTRACT

An electrical interconnection structure. The electrical structure comprises a substrate comprising electrically conductive pads and a first dielectric layer over the substrate and the electrically conductive pads. The first dielectric layer comprises vias. A metallic layer is formed over the first dielectric layer and within the vias. A second dielectric layer is formed over the metallic layer. A ball limiting metallization layer is formed within the vias. A photoresist layer is formed over a surface of the ball limiting metallization layer. A first solder ball is formed within a first opening in the photoresist layer and a second solder ball is formed within a second opening in the photoresist layer.

This application is a continuation application claiming priority to Ser. No. 11/164,107, filed Nov. 10, 2005.

BACKGROUND OF THE INVENTION

1. Technical Field

The present invention relates to an electrical connection structure and associated forming method.

2. Related Art

An electrical structure connected to another electrical structure may not comprise a structurally adequate connection. Therefore there exists a need for a means for connecting an electrical structure to another electrical structure comprising a structurally adequate connection.

SUMMARY OF THE INVENTION

The present invention provides an electrical structure, comprising:

a substrate comprising a first electrically conductive pad and a second electrically conductive pad formed within a volumetric portion of the substrate;

a first dielectric layer over a surface of said substrate, a surface of said first electrically conductive pad, and a surface of said second electrically conductive pad;

a first via and a second via in said first dielectric layer, said first via located over a portion of said surface of said first electrically conductive pad, said second via located over a portion of said surface of said second electrically conductive pad;

a metallic layer over a surface of said first dielectric layer and within said first via and said second via;

a second dielectric layer over a surface of said metallic layer, said second dielectric layer comprising a first portion removed from over and within said first via, a second portion removed from over and within said second via, and a third portion removed from between said first via and said second via;

a ball limiting metallization layer formed within said first via and said second via, over a section of said surface of said metallic layer, and over a surface of said second dielectric layer;

a first solder ball formed within and over said first via and extending laterally from said first via over and parallel to a first portion of a surface of said ball limiting metallization layer; and

a second solder ball formed within and over said second via and extending laterally from said second via over and parallel to a second portion of said surface of said ball limiting metallization layer.

The present invention advantageously provides a system and associated method for providing a structurally adequate connection means for connecting an electrical structure to another electrical structure.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 illustrates a cross sectional view of an electrical structure comprising a dielectric layer over a substrate, in accordance with embodiments of the present invention.

FIG. 2 illustrates a cross sectional view of the electrical structure of FIG. 1 after vias have been formed in the dielectric layer, in accordance with embodiments of the present invention.

FIG. 3 illustrates a cross sectional view the electrical structure of FIG. 2 after a metallic layer has been formed over the dielectric layer, in accordance with embodiments of the present invention.

FIG. 4 illustrates a cross sectional view of the electrical structure of FIG. 3 after a dielectric layer has been formed over a surface of metallic layer, in accordance with embodiments of the present invention.

FIG. 5 illustrates a cross sectional view of the electrical structure of FIG. 4 after sections of the dielectric layer have been removed, in accordance with embodiments of the present invention.

FIG. 6 illustrates a cross sectional view of the electrical structure of FIG. 5 after a ball limiting metallization (BLM) layer has been formed over the surface of metallic layer and over sections of the dielectric layer, in accordance with embodiments of the present invention.

FIG. 7 illustrates a cross sectional view of the electrical structure of FIG. 6 after a photoresist layer has been formed over a surface of the BLM layer, in accordance with embodiments of the present invention.

FIG. 8 illustrates a cross sectional view of the electrical structure of FIG. 7 after a first group of sections of the photoresist layer have been removed, in accordance with embodiments of the present invention.

FIG. 9 illustrates a cross sectional view of the electrical structure of FIG. 8 after solder structures have been formed within openings in the photoresist layer, in accordance with embodiments of the present invention.

FIG. 10 illustrates a cross sectional view of the electrical structure 2 of FIG. 9 after a second group of sections of the photoresist layer have been removed, in accordance with embodiments of the present invention.

FIG. 11 illustrates a cross sectional view of the electrical structure of FIG. 10 after sections of the BLM layer and sections of the metallic layer have been removed, in accordance with embodiments of the present invention.

FIG. 12 illustrates a cross sectional view of the electrical structure of FIG. 11 after solder balls have been formed, in accordance with embodiments of the present invention.

FIG. 13 is a flowchart illustrating an algorithm describing the process for forming the electrical structure of FIGS. 1-12, in accordance with embodiments of the present invention.

DETAILED DESCRIPTION OF THE INVENTION

FIGS. 1-12 illustrate and describe stages in a fabrication process of an electrical (interconnection) structure 2, in accordance with embodiments of the present invention. The electrical structure 2 illustrated in FIGS. 1-12 is a cross sectional view. The electrical structure 2 may comprise any electrical structure known to a person of ordinary skill in the art including, inter alia, a semiconductor device, etc. The fabrication process described with respect to FIGS. 1-12 comprises the formation of a connecting means (e.g., see solder balls 29 a and 29 b in FIG. 12) for electrically and mechanically connecting the electrical structure 2 to another electrical structure (not shown). The fabricated electrical structure 2 illustrated in FIG. 12 may comprise, inter alia, a copper back end of the line controlled collapse chip connection (CuBEOL C4) electrical structure.

In FIG. 1, the electrical structure 2 is provided for the fabrication process, in accordance with embodiments of the present invention. The electrical structure 2 comprises a substrate 5 with conductive pads 7 a ands 7 b formed within the substrate 5 and a dielectric layer 4 formed over the substrate 5. The substrate 5 may comprise any type of dielectric material used for insulating a semiconductor device 1 known to a person of ordinary skill in the art including, inter alia, a silicon dioxide substrate, a fluorinated silicon dioxide substrate, a silicon glass substrate, etc. The conductive pads 7 a ands 7 b may comprise any type of conductive pads known to a person of ordinary skill in the art including, inter alia, copper pads, etc. The conductive pads 7 a ands 7 b may be formed within the substrate 5 using any conductive pad forming process known to a person of ordinary skill in the art including, inter alia, a damascene process. A surface 6 a of the conductive pad 7 a, a surface 6 b of the conductive pad 7 b, and a surface 8 of the substrate 5 may be substantially coplanar. Note that although the dielectric layer 4 illustrated in FIGS. 1-12 only comprises one dielectric layer, the dielectric layer 4 may comprise a plurality of dielectric layers. The dielectric layer 4 may comprise any dielectric insulating material including, inter alia, oxide, nitride, or any combination thereof. The dielectric layer 4 may be deposited on the substrate 5 using any technique known to a person of ordinary skill in the art including, inter alia, a chemical vapor deposition process, etc.

FIG. 2 illustrates the electrical structure 2 of FIG. 1 after vias 9 a and 9 b have been formed, in accordance with embodiments of the present invention. Via 9 a exposes conductive pad 7 a for connection and via 9 b exposes conductive pad 7 b for connection. Vias 9 a and 9 b may be formed using any process known to a person of ordinary skill in the art including, inter alia, creating a via pattern using a standard photoresist process to create the pattern by photolithography and transferring the pattern to the dielectric layer 4 by a reactive ion etch process using a standard fluorine-containing RIE chemistry. Portions of the dielectric layer 4 are stripped away (to create vias 9 a and 9 b) using standard techniques known to a person of ordinary skill in the art.

FIG. 3 illustrates the electrical structure 2 of FIG. 2 after a metallic layer 11 has been formed, in accordance with embodiments of the present invention. The metallic layer 11 is formed over a surface 12 of the dielectric layer 4 and within vias 9 a and 9 b. The metallic layer 11 in FIG. 3 is electrically connected to conductive pads 7 a and 7 b. The metallic layer 11 may comprise any metallic conducting material including, inter alia, tantalum, tantalum nitride, etc. The metallic layer 11 may comprise a thickness T1 of at least 250 angstroms. The metallic layer 11 may be deposited over surface 12 of the dielectric layer 4 and within vias 9 a and 9 b using any deposition technique known to a person of ordinary skill in the art including, inter alia, a physical vapor deposition technique, etc.

FIG. 4 illustrates the electrical structure 2 of FIG. 3 after a dielectric layer 15 has been formed over a surface 17 of metallic layer 11, in accordance with embodiments of the present invention. The dielectric layer 15 may comprise any dielectric material including, inter alia, a polyamide dielectric material (including a photo sensitive polyamide dielectric material), an organic dielectric material, etc. The dielectric layer 15 may be formed over a surface 17 of metallic layer 11 using any process known to a person of ordinary skill in the art including, inter alia, a standard spin-apply process, etc. The dielectric layer 15 is patterned into sections 15 a . . . 15 g. The sections 15 a . . . 15 g may be patterned using any photolithographic process known to a person of ordinary skill in the art.

FIG. 5 illustrates the electrical structure 2 of FIG. 4 after removed sections 15 b, 15 d, and 15 f of the dielectric layer 15 have been removed, in accordance with embodiments of the present invention. The removed sections 15 b, 15 d, and 15 f of the dielectric layer 15 of FIG. 4 create openings 23 a . . . 23 c in FIG. 5. The sections 15 b, 15 d, and 15 f of the dielectric layer 15 may be patterned and removed using any means know to a person of ordinary skill in the art. For example, if the dielectric layer 15 comprises a negative acting photosensitive polyamide material, then sections 15 a, 15 c, 15 e, and 15 g of FIG. 4 are exposed to a light source and all sections 15 a . . . 15 g are exposed to a developer solution. Sections 15 a, 15 c, 15 e, and 15 g remain after exposure to the light source and developer solution and sections 15 b, 15 d, and 15 g (i.e., not exposed to the light source) are removed after exposure to the developer solution thereby creating openings 23 a, 23 b, and 23 c.

FIG. 6 illustrates the electrical structure 2 of FIG. 5 after a ball limiting metallization layer 19 (BLM) has been formed over surface 17 of metallic layer 11 and over sections 15 a, 15 c, 15 e, and 15 g of the dielectric layer 15, in accordance with embodiments of the present invention. The BLM layer 19 is formed over a portion of surface 17 that has been exposed in openings 23 a, 23 b, and 23 c. The BLM layer 19 may comprise a thickness T2 of about 0.5 um to about 3 um. Note that although the BLM layer 19 illustrated in FIGS. 6-12 only comprises one the layer, the BLM layer 19 may comprise a plurality of layers. BLM layer 19 may comprise any conductive material(s) including, inter alia, TiW, CrCu, Cu, or any combination thereof. BLM layer 19 may be formed using any process known to a person of ordinary skill in the art including, inter alia, a physical vapor deposition technique, a plating process, etc.

FIG. 7 illustrates the electrical structure 2 of FIG. 6 after photoresist layer 22 has been formed over surface 21 of the BLM layer 19, in accordance with embodiments of the present invention. The photoresist layer 22 may comprise an organic photoresist layer. The photoresist layer 22 is patterned into sections 22 a . . . 22 e. The sections 22 a . . . 22 e may be patterned using any photolithographic process known to a person of ordinary skill in the art.

FIG. 8 illustrates the electrical structure 2 of FIG. 7 after sections 22 b and 22 d of the photoresist layer 22 have been removed, in accordance with embodiments of the present invention. The removed sections 22 b and 22 d of the photoresist layer 22 of FIG. 7 creates openings 27 a and 27 b in FIG. 8. The section 22 b and 22 d of the photoresist layer 22 may be removed using any photolithographic process know to a person of ordinary skill in the art.

FIG. 9 illustrates the electrical structure 2 of FIG. 8 after solder structures 25 a and 25 b have been formed within openings 27 a and 27 b respectively, in accordance with embodiments of the present invention. The solder structure 25 a is electrically connected to the BLM layer 19 and ultimately to conducive pad 7 a. The solder structure 25 b is electrically connected to the BLM layer 19 and ultimately to conducive pad 7 b. The solder structures 25 a and 25 b may be formed using any solder structure forming process know to a person of ordinary skill in the art including, inter alia, an electroplating process, etc. The solder structures 25 a and 25 b may comprise any solder material composition including, inter alia, a lead/tin composition, a lead free composition (e.g., a tin /copper composition, a tin/silver composition, etc.), etc.

FIG. 10 illustrates the electrical structure 2 of FIG. 9 after sections 22 a, 22 c, and 22 e have been removed, in accordance with embodiments of the present invention. The removed sections 22 a, 22 c, and 22 e from FIG. 9 creates openings 30 a, 30 b, and 30 c respectively in FIG. 10. The sections 22 a, 22 c, and 22 e may be removed using, inter alia, a standard wet chemistry etch, etc.

FIG. 11 illustrates the electrical structure 2 of FIG. 10 after sections of the BLM layer 19 and sections of the metallic layer 11 have been removed, in accordance with embodiments of the present invention. Sections of the BLM layer 19 within openings 30 a, 30 b, and 30 c have been removed. Sections of the metallic layer 11 within openings 30 a, 30 b, and 30 c have been removed. Any etching process may be used to remove the sections of the BLM layer 19 within openings 30 a, 30 b, and 30 c including, inter alia, a wet etch process, a reactive ion etch process, etc. Any etching process may be used to remove the sections of the metallic layer 11 within openings 30 a, 30 b, and 30 c including, inter alia, an industry standard dry reactive ion etch process containing fluorine. Removing the sections of the BLM layer 19 and the sections of the metallic layer 11 within opening 30 b electrically separates the solder structures 25 a and 25 b from each other.

FIG. 12 illustrates the electrical structure 2 of FIG. 11 after solder balls 29 a and 29 b have been formed, in accordance with embodiments of the present invention. Solder ball 29 a is formed from solder structure 25 a and solder ball 29 b is formed from solder structure 25 b. The solder structures 25 a and 25 b are treated in a high temperature (e.g., 150C-380C) reflow furnace to generate the solder balls 29 a and 29 b. The solder balls 29 a and 29 b may be cleaned with an industry standard cleaning process such as, inter alia, using a dilute acid rinse to remove surface oxides from the solder balls 29 a and 29 b. The electrical structure 2 of FIG. 12 is ready for electrically and mechanically connecting to another electrical structure (not shown).

FIG. 13 is a flowchart a process for forming the electrical structure 2 of FIGS. 1-12, in accordance with embodiments of the present invention. In step 42, an electrical structure 2 is provided for a fabrication process. The electrical structure 2 comprises a substrate 5 with conductive pads 7 a ands 7 b formed within the substrate 5 and a dielectric layer 4 formed over the substrate 5. In step 44, the vias 9 a and 9 b are formed within the dielectric layer 4. In step 46, the metallic layer 11 is formed over surface 12 of the dielectric layer 4 and within vias 9 a and 9 b. In step 48, dielectric layer 15 is formed over surface 17 of the metallic layer 11. In step 50, sections 15 b, 15 d, and 15 f of the dielectric layer are removed thereby creating openings 23 a . . . 23 c. In step 52, the BLM layer 19 is formed over surface 17 of metallic layer 11 and over sections 15 a, 15 c, 15 e, and 15 g of the dielectric layer 15. In step 54, photoresist layer 22 is formed over surface 21 of the BLM layer 19. In step 56, sections 22 b and 22 d of the photoresist layer 22 are removed. The removed sections 22 b and 22 d of the photoresist layer 22 form openings 27 a and 27 b. In step 58, solder structures 25 a and 25 b are formed within openings 27 a and 27 b respectively. In step 60, sections 22 a, 22 c, and 22 e of the photoresist layer 22 are removed. The removed sections 22 a, 22 c, and 22 e form openings 30 a, 30 b, and 30 c respectively. In step 62, solder balls 29 a and 29 b are formed. In step 64, solder balls 29 a and 29 b are cleaned to remove surface oxides.

While embodiments of the present invention have been described herein for purposes of illustration, many modifications and changes will become apparent to those skilled in the art. Accordingly, the appended claims are intended to encompass all such modifications and changes as fall within the true spirit and scope of this invention. 

1. An electrical structure, comprising: a substrate comprising a first electrically conductive pad and a second electrically conductive pad formed within a volumetric portion of the substrate; a first dielectric layer over a surface of said substrate, a surface of said first electrically conductive pad, and a surface of said second electrically conductive pad; a first via and a second via in said first dielectric layer, said first via located over a portion of said surface of said first electrically conductive pad, said second via located over a portion of said surface of said second electrically conductive pad; a metallic layer over a surface of said first dielectric layer and within said first via and said second via; a second dielectric layer over a surface of said metallic layer, said second dielectric layer comprising a first portion removed from over and within said first via, a second portion removed from over and within said second via, and a third portion removed from between said first via and said second via; a ball limiting metallization layer formed within said first via and said second via, over a section of said surface of said metallic layer, and over a surface of said second dielectric layer; a first solder ball formed within and over said first via and extending laterally from said first via over and parallel to a first portion of a surface of said ball limiting metallization layer; and a second solder ball formed within and over said second via and extending laterally from said second via over and parallel to a second portion of said surface of said ball limiting metallization layer.
 2. The electrical structure of claim 1, further comprising: an opening in said ball limiting metallization layer and said metallic layer, said opening located between said first solder ball and said second solder ball.
 3. The electrical structure of claim 1, wherein said first solder ball is electrically connected to said first electrically conductive pad, and wherein said second solder ball is electrically connected to said second electrically conductive pad.
 4. The electrical structure of claim 1, wherein said first dielectric layer comprises more than one layer of dielectric material.
 5. The electrical structure of claim 1, wherein said metallic layer comprises a material selected from the group consisting of tantalum and tantalum nitride.
 6. The electrical structure of claim 1, wherein said second dielectric layer comprises a polyamide layer.
 7. The electrical structure of claim 1, wherein said metallic layer comprises a thickness at least 250 angstroms.
 8. The electrical structure of claim 1, wherein each of said first solder ball and said second solder ball comprises a substantially lead free solder composition.
 9. The electrical structure of claim 1, wherein said first dielectric layer and said second dielectric layer each comprise a different dielectric material. 